Flame retardant cotton canvas fabric

Cotton flame retardant fabric is made of 100% natural fibre "cotton weaving finishing, it has the air permeability, moisture absorption quick drying, soft, soft luster, but also retain the characteristics of the cotton fiber antistatic ecological environmental protection. Use the fabrics made of protective clothing, wearing comfortable, breathable moisture permeability, no stimulation to the skin, is pay attention to the natural environmental characteristics of the customer's first choice.

Flame retardant cotton surface is on the basis of cotton dyed fabric flame retardant processing so as to achieve the flame retardant fabric, flame retardant treatment technology are mainly PROBAN, PYROAVTEX, etc.

Flame retardant cotton fabric according to different grain can be divided into: the flame retardant cotton plain cloth, the flame retardant cotton yarn card, flame retardant cotton satin drill and flame retardant cotton canvas.

At present the most popular in the international flame retardant finishing is generally two Plutarch benzene flame retardant and CP.

Flame retardant fabrics in Plutarch benzene flame retardant, for example, using the most authoritative international Proban flame retardants, it is a kind of used for the durability of cotton fiber and its blended fabric finishing fire retardant, its main characteristic is to use this kind of flame retardant finishing after production, the fabric form within the permanent crosslinking, thus has the durability of the flame retardant performance, can wash more than 50 times. The flame retardant fabric can effectively prevent flame spread, can maintain the original performance of fabric. Flame retardant performance can be achieved EN470-1 EN531 EN533 NFPA2112.

Cotton flame retardant fabric testing

A) any testing sample after lighting the combustion should not have spread to the fabric edge or fabric upper.

B) in any test sample, lighting it and should not have holes to form.

C) in any test sample, should not be lit burning molten drops or melt down.

D) spreading combustion time must be less than or equal to 2 seconds.

E) smouldering time must be less than or equal to 2 seconds.